Title: Matriz tridimensional con potencial para regeneración ósea
Adviser: Echeverri-Cuartas, C. E. (Claudia Elena)
Issue Date: 13-Apr-2014
Abstract: Biodegradable polymeric scaffolds for tissue engineering have received much attention in recent years since they provide a temporal and spatial environment for cellular growth and interactions besides the formation of the extracellular matrix, supporting the formation of new tissue. A pre-fabricated scaffold can either act as a supportive prosthetic material to regenerate tissue in vivo, or as a cell adhesive substratum to form engineered tissue in vitro. The following work presents the synthesis of three-dimensional PLLA (polylactic acid) scaffolds produced by a salt leaching/gas foaming method and their respective morphological and mechanical characterization by techniques such as: swelling, SEM microscopy, optical microscopy and compression assays.
Description: Las matrices poliméricas han recibido gran atención en los últimos años, ya que proporcionan un entorno temporal para el crecimiento y la interacción celular, además de la formación de la matriz extracelular, dando soporte a la formación de un nuevo tejido al actuar como un material prostético para regenerar tejido in vivo o como sustrato adhesivo celular para formar tejidos in vitro. El siguiente trabajo presenta la obtención de matrices tridimensionales de PLLA (ácido poliláctico) por medio del método salt leaching/gas foaming y la caracterización morfológica y mecánica de las mismas, mediante técnicas que incluyen hinchamiento, microscopia SEM, microscopia óptica y ensayos mecánicos de compresión.
URI: http://hdl.handle.net/11190/334
Appears in Collections:Ingeniería Biomédica

Files in This Item:
File Description SizeFormat 
BIOM0189.pdf6.01 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons