Fabricación y caracterización de una matriz tridimensional de Hidroxiapatita Macroporosa para aplicación en ingeniería de tejidos óseos
Artículo de revista
2014-05-08
Biomédica, Mecatrónica y Mecánica
Bone tissue engineering came up as a new option treatment for different kinds of illness, among them
bone diseases. All this development has allowed solving multiple medical problems. The development of a
hydroxyapatite scaffold for bone cells culture will be another alternative to attend several diseases that are
caused on bones and that usually lead to disabilities in people. In this study synthetic hydroxyapatite was produced
by a precipitation route with amonium phosphate (NH4H2PO4) and calcium nitrate (Ca(NO3)2*4H2O)
as precursors.
La ingeniería de tejido óseo surge como una nueva opción para el tratamiento de muchos tipos de
afecciones, entre ellas las enfermedades óseas, permitiendo resolver múltiples problemas en el área médica.
El desarrollo de una matriz de hidroxiapatita para cultivo de células óseas permitirá contar con otra alternativa
para enfrentar las enfermedades causadas en el hueso y articulaciones que frecuentemente llevan a la
discapacidad en las personas. En este trabajo se obtuvo hidroxiapatita sintética por la ruta de precipitación
a partir de fosfato de amonio NH4H2PO4 y nitrato de calcio Ca(NO3)2
.4H2O.