Evaluation of HMA cracking resistance as a function of laboratory aging based on the direct-tension test

Vista sencilla de ítem
dc.contributor.authorWalubita, Lubinda F.spa
dc.contributor.authorFlórez, Blanca L.spa
dc.contributor.authorÁlvarez, Allex E.spa
dc.creator.emaill-walubita@ttimail. tamu.eduspa
dc.creator.emailelvica-25@hotmail.comspa
dc.creator.emailaalvarez@unimagdalena.edu.cospa
dc.date.accepted2012-06-19spa
dc.date.accessioned2013-11-13T19:50:49Zspa
dc.date.available2013-11-13T19:50:49Zspa
dc.date.created2012-07spa
dc.date.issued2013-11-13spa
dc.date.submitted2011-08-31spa
dc.descriptionHot mix asphalt (HMA) is a heterogeneous composite material of asphalt-binder, aggregates, air voids, and other additives including lime, fibers, etc., predominantly used for pavement construction. With time, the HMA mix ages, which leads to changes in the material properties and response behavior. This paper documents a laboratory study that was conducted to evaluate the suitability of the direct-tension (DT) test to assess the effects of asphalt-binder aging on the HMA mix fracture properties and cracking-resistance potential. Two dense-graded HMA mixes were subjected to different laboratory aging exposure conditions and then tested with the DT test. From this test, the HMA mix fracture response was characterized in terms of the tensile strength, tensile strain at peak failure load, stiffness, and fracture energy. Overall, the results indicated that asphalt-binder aging has a detrimental effect on the fracture response and cracking-resistance of HMA mixes, which can be captured based on the DT test. Therefore, the asphalt-binder aging needs to be considered and properly accounted for during the material design and analysis stages of HMA mixes. However, research with more HMA mixes and correlation with field data is strongly recommended to validate the laboratory findings reported in this paper.spa
dc.description.abstractLa mezcla asfáltica en caliente (MAC) es un material compuesto, heterogéneo, integrado por cemento asfáltico (o asfalto), agregados, vacíos y otros aditivos incluyendo cal, fibras, etc., usado predominantemente para la construcción de pavimentos. A lo largo del tiempo, la MAC sufre envejecimiento, lo cual conlleva cambios en las propiedades del material y en su respuesta. Este artículo documenta un estudio de laboratorio llevado a cabo para evaluar la posibilidad de emplear el ensayo de tensión directa (TD) para determinar los efectos del envejecimiento del asfalto sobre las propiedades de fractura y resistencia al agrietamiento de MAC. Dos MAC de gradación densa fueron sometidas a diferentes condiciones de envejecimiento en laboratorio y luego sometidas al ensayo de TD. A partir de este ensayo, el comportamiento ante fractura se caracterizó en términos de la resistencia a tensión, deformación unitaria de tensión a la carga de falla, rigidez y energía de fractura. En general, los resultados indicaron que el envejecimiento por oxidación del asfalto tiene un efecto negativo sobre la respuesta ante fractura y la resistencia al agrietamiento de la MAC, el cual puede ser captado por medio del ensayo de TD. Por lo tanto, el envejecimiento del asfalto debe ser considerado y cuantificado en forma adecuada durante el diseño y análisis de la MAC. Sin embargo, se recomienda adelantar investigación adicional con otras mezclas y correlacionar resultados con datos de campo para validar la información de laboratorio reportada en este artículo.spa
dc.format.extent16 p.spa
dc.format.mimetypeapplication/pdfspa
dc.identifier.bibliographiccitationWalubita, L. F., Flórez, B. L., and Álvarez, A. E. (2012). Evaluation of HMA cracking resistance as a function of laboratory aging based on the direct-tension test, Revista EIA, 9 (17), 209-224. doi: http://hdl.handle.net/11190/138spa
dc.identifier.issnISSN 17941237spa
dc.identifier.urihttps://repository.eia.edu.co/handle/11190/138spa
dc.language.isoengspa
dc.publisher.editorFondo Editorial EIAspa
dc.relation.ispartofRevista EIAspa
dc.relation.referencesAASHTO. Standard specifications for transportation materials and methods of sampling and testing. Designation: PP2, Standard practice for short and long term aging of hot mix asphalt. Washington D.C., 1994.spa
dc.relation.referencesAirey, G. D. (2003). “State of the art report on ageing test methods for bituminous pavement materials”. International Journal of Pavement Engineering, vol. 4, No. 3, pp. 165-176.spa
dc.relation.referencesArenas, H. L. Tecnología del cemento asfáltico. Popayán: Faid, 2005.spa
dc.relation.referencesAsphalt Rehab: [consulted on June 11, 2012] Available in: <http://www.asphaltrehab.com/infrared.html>.spa
dc.relation.referencesDomke, C. H.; Davison, R. R. and Glover, C. J. (2000). “Effect of oxygen pressure on asphalt oxidation kinetics”. Industrial & Engineering Chemistry Research, vol. 39, No. 3, pp. 592-598.spa
dc.rightsDerechos Reservados - Universidad EIA, 2020spa
dc.rights.accessrightsinfo:eu-repo/semantics/openAccessspa
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2spa
dc.rights.creativecommonsAtribución-NoComercialspa
dc.rights.licenseEl autor de la obra, actuando en nombre propio, hace entrega del ejemplar respectivo y de sus anexos en formato digital o electrónico y autoriza a la ESCUELA DE INGENIERIA DE ANTIOQUIA, para que en los términos establecidos en la Ley 23 de 1982, Ley 44 de 1993, Decisión andina 351 de 1993, Decreto 460 de 1995, y demás normas generales sobre la materia, utilice y use por cualquier medio conocido o por conocer, los derechos patrimoniales de reproducción, comunicación pública, transformación y distribución de la obra objeto del presente documento. PARÁGRAFO: La presente autorización se hace extensiva no sólo a las dependencias y derechos de uso sobre la obra en formato o soporte material, sino también para formato virtual, electrónico, digital, y en red, internet, extranet, intranet, etc., y en general en cualquier formato conocido o por conocer. EL AUTOR, manifiesta que la obra objeto de la presente autorización es original y la realiza sin violar o usurpar derechos de autor de terceros, por lo tanto la obra es de exclusiva autoría y tiene la titularidad sobre la misma. PARÁGRAFO: En caso de presentarse cualquier reclamación o acción por parte de un tercero en cuanto a los derechos de autor sobre la obra en cuestión, EL AUTOR, asumirá toda la responsabilidad, y saldrá en defensa de los derechos aquí autorizados; para todos los efectos la ESCUELA DE INGENIERÍA DE ANTIOQUIA actúa como un tercero de buena fe.spa
dc.rights.urihttps://creativecommons.org/licenses/by-nc/4.0/spa
dc.subject.arcmarcMATERIALES DE CONSTRUCCIÓNspa
dc.subject.arcmarcBUILDING MATERIALSspa
dc.subject.arcmarcPAVIMENTOS DE ASFALTOspa
dc.subject.arcmarcPAVEMENTS , ASPHALTspa
dc.subject.eiaINFRAESTRUCTURA Y GESTIÓN DEL TERRITORIOspa
dc.subject.eiaINFRAESTRUCTURE AND LAND PLANNINGspa
dc.subject.keywordsASPHALT - BINDERspa
dc.subject.keywordsHOT MIX ASPHALT ( HMA )spa
dc.subject.keywordsAGINGspa
dc.subject.keywordsFRACTUREspa
dc.subject.keywordsCRACKINGspa
dc.subject.keywordsCEMENTO ASFÁLTICOspa
dc.subject.keywordsMEZCLA ASFÁLTICA EN CALIENTEspa
dc.subject.keywordsENVEJECIMIENTOspa
dc.subject.keywordsFRACTURAspa
dc.subject.keywordsAGRIETAMIENTOspa
dc.subject.lcshREI00187spa
dc.titleEvaluation of HMA cracking resistance as a function of laboratory aging based on the direct-tension testspa
dc.title.alternativeAvaliação da resistência as rachaduras de misturas asfálticas em quente em função de seu envelhecimento a partir do ensaio de tensão diretaspa
dc.title.alternativeEvaluación de la resistencia al agrietamiento de mezclas asfálticas en caliente en función de su envejecimiento a partir del ensayo de tensión directaspa
dc.typeArtículo de revistaspa
dc.type.coarhttp://purl.org/coar/resource_type/c_6501spa
dc.type.coarversionhttp://purl.org/coar/version/c_970fb48d4fbd8a85spa
dc.type.contentTextspa
dc.type.driverinfo:eu-repo/semantics/articlespa
dc.type.redcolhttps://purl.org/redcol/resource_type/ARTspa
dc.type.versioninfo:eu-repo/semantics/publishedVersionspa
dspace.entity.typePublication
Archivos
Bloque original
Mostrando 1 - 1 de 1
Miniatura
Nombre:
REI00187.pdf
Tamaño:
2.09 MB
Formato:
Adobe Portable Document Format
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
Miniatura
Nombre:
license.txt
Tamaño:
1.46 KB
Formato:
Item-specific license agreed upon to submission
Descripción:
Descargar
Colecciones
Revista EIA