Publicación: Síntesis y caracterización de hidrogeles de alcohol polivinílico por la técnica de congelamiento/descongelamiento para aplicaciones médicas
Portada
Cargando...
Citas bibliográficas
Código QR
LA Referencia Stats
Autor corporativo
Recolector de datos
Otros/Desconocido
Director audiovisual
Editor/Compilador
Editores
Tipo de Material
Fecha
2013-11-26
Cita bibliográfica
Título de serie/ reporte/ volumen/ colección
Es Parte de
Revista EIA
Resumen en español
Using different cycles of freeze-thawing, semicrystalline polyvinyl alcohol hydrogels were synthesized in concentrations of 7.5 % and 12 %. The kinetic and grade of swelling, states of water and the tensile strength were calculated by gravimetry, by differential scanning calorimetry, DSC, and the tensile tests respectively. The results show that hydrogels with less concentration and cycles have better grade and kinetic of swelling, while the tensile strength is lower. The DSC results allow us to determine the free and freezable bound waters in our hydrogels. The characteristics obtained from these hydrogels lead their classification for different medical applications.
Descripción general
Usando diferentes ciclos de congelamiento/descongelamiento se prepararon hidrogeles de alcohol polivinílico semicristalino 7,5 % y 12 % en concentración. La cinética y el grado de hinchamiento, los estados del agua y la resistencia a la tracción se evaluaron por gravimetría, calorimetría diferencial de barrido (DSC) y pruebas de tracción, respectivamente. Los resultados indican que los hidrogeles de menor concentración y con menor número de ciclos presentan cinética y grado de hinchamiento mejores y menor resistencia a la tracción. Las DSC permitieron determinar la presencia de agua libre y de agua vinculada congelable. Las características de estos hidrogeles permiten clasificarlos para diferentes aplicaciones médicas.